Project contact is Hyungsuk Lim at Mississippi State University
This project aims to develop the preservative-treatment procedures for industrial cross-laminated timber (CLT) mats composed of southern yellow pine (SYP) lumber. The feasibility of pre- and post-treating CLT panels with an environment-friendly preservative system for ground-contact applications at an industrial scale will be evaluated from adhesion, mechanical, and durability performance aspects. As for the pre-treatment method, CLT panels will be consolidated with preservative-treated lumber adopting industrial CLT manufacturing parameters, including glue-type and clamping pressure. Alternatively, conventional CLT panels will be pressure treated with the same preservative system and dried afterward. As one of the primary focuses of the research, drying schedules which would not damage wood or adhesive layers will be determined. Also, penetration and retention of the preservatives throughout the post-treated panels will be analyzed. Adhesion and mechanical performance of the treated panels will be evaluated according to industry-accepted standards. Durability performance of the treated panels will be examined through laboratory weathering and on-site field tests.
Effective preservative treatments for Canadian glulam products are needed to maintain markets for mass timber on building facades, access markets with significant termite hazards, and expand markets for wood bridges. For all three applications, borate-treatment of lamina before gluing would be preferred as it would lead to maximum preservative penetration. However, the need to plane after treatment and prior to gluing removes the best-treated part of the wood, and creates a disposal issue for treated planer shavings. The present research evaluates the block shear resistance of glulam prepared from untreated and borate-treated lamina with a polyurethane adhesive. Borate treatment was associated with a small but statistically significant loss in median shear strength when evaluated dry; however, there was no difference between the performance of untreated and borate-treated samples when exposed to the vacuum-pressure soak/dry or the boil-dry-freeze/dry procedures. Further work is needed to modify the composition or application of the resin to improve shear strength for glulam applications and ensure consistent performance. However, overall, these data indicate that samples prepared from borate-treated lamina perform similarly in terms of block shear resistance to those prepared from untreated lamina.
Field tests of untreated and preservative-treated glulam beams in outdoor exposure, in ground contact and above ground, were inspected for decay after five years. Copper azole and ACQ-D-treated material was in excellent condition, while moderate to severe decay was present in untreated non-durable material. Early stages of decay were also noted in yellow cedar glulam in the above-ground test. Using galvanized rather than stainless steel fasteners appeared to have a protective effect against decay in untreated material, supporting the hypothesis that zinc from the sacrificial coating on galvanized bolts inhibits germination of basidiospores.
Glulam manufactured from laminating stock of three species pre-treated with ACQ-D or CA was exposed outdoors in an above-ground field test using a modified post and rail test design. After six years’ exposure, early to moderate decay was found in untreated test units, while those which were preservative-treated were completely sound.
Timber construction has become completely modernized. It has gained considerably in market share with respect to competing building materials and is dominated by systems such as frame and solid timber construction.
Every timber construction is determined by its structure. Hence it is essential to know the connections and relationships from the design stage right through to the construction phase. Systems in Timber Engineering takes a whole new approach to this subject. It is a comprehensive, analytical, and visually organized treatment, from the simple single-family house to the large-scale multistore structure. It includes the building envelope, which is so important for saving energy, and systems for ceilings and interior dividing walls, which are so essential from the vantage point of construction.
This work uses plans, schematic drawings, and pictures to show the current and forward-looking state of the technology as applied in Switzerland, a leading country in the field of timber construction.
Cross-laminated timber (CLT) may require preservative treatment in markets with severe termite hazards. Given the size of CLT panels, conventional pressure treatment would not be feasible. We therefore assessed the treatability of CLT panels with an alternative low moisture uptake surface-applied penetrating process for applying termiticides. Hem-fir panels were selected for the initial tests on the grounds that western hemlock and amabilis fir are relatively treatable. Nine test panels were dip treated and stored for 7, 14, or 21 day activation periods. Borate retention ranged from 1.2 to 6.5 kg/m3 and penetration ranged from 3 to 9 mm. Longer activation periods did not result in improved penetration. Greater penetration would likely be needed to meet performance-based standards.
Summarizes information on wood as an engineering material. Presents properties of wood and wood-based products of particular concern to the architect and engineer. Includes discussion of designing with wood and wood-based products along with some pertinent uses. Keywords: wood structure, physical properties (wood), mechanical properties (wood), lumber, wood-based composites, plywood, panel products, design, fastenings, wood moisture, drying, gluing, fire resistance, finishing, decay, preservation, wood-based products, heat sterilization, sustainable use.